Process: FFF - Fused Filament Fabrication
TPU-85 is a 85 Shore A flexible filament used in the FFF 3D printing process. Its low durometer makes it ideal for parts that need to bend and stretch while still being able to retain it's shape. Applications for this material could include Seals, gaskets, and plugs.

MECHANICAL PROPERTIES TEST METHOD METRIC IMPERIAL
Tensile Modulus ASTM D638 12 MPa 1800 psi
Tensile Stress at Yield ASTM D638 4 Mpa 580 psi
Tensile Stress, Ultimate ASTM D638 26 Mpa 3700 psi
Elongation at Yield ASTM D638 65% 65%
Elongation at Break ASTM D638 660% 660%
Toughness ASTM D638 82.7 m·N/m3 x106 12,000 in·lbF/in3
Izod Impact Strength ASTM D256 4.2 kJ/m² 2 ft lb/in2
Moisture Absorption (24 hours) ASTM D570 .22% .22%
Hardness Durometer 85 Shore A 85 Shore A
Colors   Request Avalability Request Avalability
THERMO PROPERTIES TEST METHOD METRIC IMPERIAL
Glass Transition (Tg) DSC -35 deg. C -31 deg. F
H.D.T. @ 0.07 Mpa (10.75 psi) ASTM D648 60 deg. C 140 deg. F
H.D.T. @ 0.45 Mpa (66 psi)  ASTM D648 44 deg. C 111 deg. F
Note: Materials specified are stocked materials, other materials may be avaiable upon request. The information on the material properties are obtained from the material manfucture and SICAM expressly disclaims any product warranties and cannot guarantee the accuracy of the information presented.

tpu95

Download specs
Process: FFF - Fused Filament Fabrication
TPU-95 is a 95 Shore A semi-flexible filament used in the FFF 3D printing process. This material has an impact strength 84% greater than ABS, abrasion resistance 40% higher than ABS and 76% higher than PLA, and 580% Elongation capabilities. Applications for this material could include grips, guides, hinges, sleeves & snap-fit parts.

MECHANICAL PROPERTIES TEST METHOD METRIC IMPERIAL
Tensile Modulus ASTM D638 26 MPa 3800 psi
Tensile Stress at Yield ASTM D638 9 Mpa 1250 psi
Tensile Stress, Ultimate ASTM D638 39 Mpa 5650 psi
Elongation at Yield ASTM D638 55% 55%
Elongation at Break ASTM D638 580% 580%
Toughness ASTM D638 117.2 m·N/m3 x106 17,000 in·lbF/in3
Izod Impact Strength ASTM D256 19.1 kJ/m² 9.1 ft lb/in2
Moisture Absorption (24 hours) ASTM D570 .18% .18%
Hardness Durometer 95 Shore A 95 Shore A
Colors   Request Avalability Request Avalability
THERMO PROPERTIES TEST METHOD METRIC IMPERIAL
Glass Transition (Tg) DSC -24 deg. C -11 deg. F
H.D.T. @ 0.07 Mpa (10.75 psi) ASTM D648 74 deg. C 165 deg. F
H.D.T. @ 0.45 Mpa (66 psi)  ASTM D648 49 deg. C 120 deg. F
Note: Materials specified are stocked materials, other materials may be avaiable upon request. The information on the material properties are obtained from the material manfucture and SICAM expressly disclaims any product warranties and cannot guarantee the accuracy of the information presented.

abs

Download specs
Process: FFF - Fused Filament Fabrication
ABS is a filament used in the FFF process to produce a strong and tough part with its exceptional mechanical properties. Our FFF ABS can be used for a wide range of applications, such as prototyping for injection molding ABS parts.

MECHANICAL PROPERTIES TEST METHOD METRIC IMPERIAL
Tensile Modulus ISO 527 1681.5 MPa 243 ksi
Tensile Stress at Yield ISO 527 39 MPa 5656 psi
Tensile Stress at Break ISO 527 33.9 MPa 4916 psi
Elongation at Yield ISO 527 3.50% 3.50%
Elongation at Break ISO 527 4.8% 4.8%
Flexural Strength ISO 178 70.5 MPa 10225 psi
Flexural Modulus ISO 178 2070 MPa 300 ksi
Izod Impact Strength ISO 180 10.5 kJ/m² 5 ft lb/in²
Hardness Durometer 76D 76D
Colors   Request Avalability Request Avalability
THERMO PROPERTIES TEST METHOD METRIC IMPERIAL
Vicat Softening ISO 306 97 deg. C 206 deg. F
Note: Materials specified are stocked materials, other materials may be avaiable upon request. The information on the material properties are obtained from the material manfucture and SICAM expressly disclaims any product warranties and cannot guarantee the accuracy of the information presented.

pla

Download specs
Process: FFF - Fused Filament Fabrication
PLA or Polylactic Acid is a filament specifically made for FFF 3D printing. Regular PLA is generally strong material but under certain circumstances can be considered brittle. With this high strength PLA, those negative qualities have been eliminated and has very similar mechanical properties to that of ABS filament for the FFF process. PLA part applications can be used for initial durable prototypes to test form and fit.

MECHANICAL PROPERTIES TEST METHOD METRIC IMPERIAL
Young's Modulus ASTM D638   1879 Mpa   272.5 ksi
Tensile Strength ASTM D638   28.1 Mpa   4075.5 psi
Elongation at Break ASTM D638   1.36%   1.36%
Bending Modulus ASTM D790   2119 Mpa   307.3 ksi
Bending Strength ASTM D790   48 MPa   6.9 ksi
Impact Strength ASTM D256 12.15 kJ/m²  5.78 ft lb/in²
Colors   Request Avalability Request Avalability
THERMAL PROPERTIES TEST METHOD METRIC IMPERIAL
Glass Transition Temperature (TG)   DSC, 10°C/min   50-60 °C   122-140 °F
Note: Materials specified are stocked materials, other materials may be avaiable upon request. The information on the material properties are obtained from the material manfucture and SICAM expressly disclaims any product warranties and cannot guarantee the accuracy of the information presented.

petg

Download specs
Process: FFF - Fused Filament Fabrication
PETG is a styrene free material created specifically for FFF 3D printing. This is a very tough and durable material with great mechanical properties. Applications of this material are for prototype parts and in some cases end use parts that are durable and functional.

MECHANICAL PROPERTIES TEST METHOD METRIC IMPERIAL
Tensile Stress at Yield ASTM D 638   50 MPa 7210 psi
Tensile Stress at Break ASTM D 638 35 MPa 6240 psi
Elongation at Yield ASTM D 638   4.50%   4.50%
Elongation at Break ASTM D 638   193.00% 193.00%
Flexural Strength ASTM D 790 1800 MPa 261 ksi
Flexural Modulus ASTM D 256 67 MPa 9719 psi
Izod Impact Strength, Notched ASTM D 256 70 J/m 1.3 ft lb/in
Hardness Durometer 105 R (Rockwell) 105 R (Rockwell)
Colors   Request Avalability Request Avalability
THERMO PROPERTIES TEST METHOD METRIC IMPERIAL
H.D.T. @ 0.455 Mpa (66 psi) ASTM D 648 71 deg. C 160 deg. F
H.D.T. @ 1.82 Mpa (264 psi) ASTM D 648 63 deg. C 145 deg. F
Note: Materials specified are stocked materials, other materials may be avaiable upon request. The information on the material properties are obtained from the material manfucture and SICAM expressly disclaims any product warranties and cannot guarantee the accuracy of the information presented.