| Somos® DMX SL-100 |
DMX-SL Technology |
|
High Impact, Durable SLA Rapid Prototyping Material
DMX-SL100 parts are extreamly tough and are ideal for large part designs that require high impact strength and durability. Somos® DMX-SL100 produces parts that demonstarate an unprecedented combination of toughness and impact strenght that are far superior to competing technologies that utilize molten or sintered thermoplastics.
DMX-SL100 parts simulates production materials and are ideal for functional testing.
Color: Ivory
|
|
|
| Applications |
|
Market Segments |
|
High Impact
Enclosures
Large Part Designs
Snap Fits
Large Part Designs
|
|
Aerospace
Automotive
Consumer Products
Industrial
Telecommunications
|
|
| |
Mechanical Properties |
|
| ASTM Method |
Property Description |
Metric |
Imperial |
| D638M |
Tensile Modulus |
2,260 - 2,560 Mpa |
327,000 - 371,000 psi |
| D638M |
Tensile Strength at Break |
27.7 - 32.1 Mpa |
4,300 - 4,700 psi |
| D638M |
Tensile Strength at Yield |
41.1 - 45.5 Mpa |
6,400 - 6,600 psi |
| D638M |
Elongation at Break |
12 - 28% |
12 - 28% |
| D638M |
Elongation at Yield |
4% |
4% |
| D638M |
Poisson's Ratio |
.40 - .42 |
.40 - .42 |
| D790M |
Flexural Strength |
68.0 Mpa |
9,800 - 9,900 psi |
| D790M |
Flexural Modulus |
2,280 - 2,300 Mpa |
331,000 - 333,000 psi |
| D2240 |
Hardness (Shore D) |
80 |
80 |
| D256A |
Izod Impact (Notched) |
.61 - .71 J/cm |
1.15 - 1.32 ft-lb/in |
| D570-98 |
Water Absorption |
..82 - .85% |
.82 - .85% |
|
| |
Electrical / Thermal Properties |
|
| ASTM Method |
Property Description |
Metric |
Imperial |
| E831-05 |
C.T.E. 40°C - 0°C (-40°F - 32°F) |
83.8 - 85.2 mm/m°C |
46.6 - 47.3 min/in°F |
| E831-05 |
C.T.E. 0°C - 50°C (32°F - 122°F) |
124.0 - 134.1 mm/m°C |
68.9 - 74.5 min/in°F |
| E831-05 |
C.T.E. 50°C - 100°C (122°F - 212°F) |
181.2 - 185.3 mm/m°C |
100.7 - 102.9 min/in°F |
| E831-05 |
C.T.E. 100°C - 150°C (212°F - 302°F) |
178.4 - 179.9 mm/m°C |
99.1 - 99.9 min/in°F |
| D150-98 |
Dielectric Constant 60 Hz |
4.3 |
4.3 |
| D150-98 |
Dielectric Constant 1KHz |
3.9 |
3.9 |
| D150-98 |
Dielectric Constant 1MHz |
3.7 |
3.7 |
| D149-97a |
Dielectric Strength |
14.1 - 15.8 kV/mm |
357 - 400 V/mil |
| E1545-00 |
Tg |
37°C |
99°F |
| D648 |
HDT @ 0.46 Mpa (66 psi) |
44°C |
112°F |
| D648 |
HDT @ 1.81 Mpa (264 psi) |
41°C |
106°F |
|
|
Note: The information on the material properties was obtained from DSM Somos, a unincorporated subsidiary of DSM Desotech Inc. Somos is a registered tradmark of DSM Somos. SICAM Corporation expressly disclaims any product warranties and cannot garantee the accuracy of the information presented.
|
|